不同粒径级配的废玻璃沥青混合料性能的试验研究

李烽

摘要：对不同粒径级配的废玻璃掺量对沥青混合料的性能影响进行了试验研究，分析比较其相对密度、空隙率、矿料间隙率、沥青饱和度、马歇尔稳定度及流值。结果表明，玻璃集料的级配对沥青混合料的性能具有较大影响，随其粒径的增大，玻璃沥青混合料的空隙率、矿料间隙率、流值趋于减小，而沥青饱和度、残留稳定度则不断增大；当玻璃粒径达到4.75mm档时，稳定度达到最大值，而其余各值仍在规范要求范围之内。

关键词：废玻璃；粒径级配；沥青混合用性能；

Experimental Investigation on Asphalt Mixture Properties with Waste Glass of Different Particle Size and Gradation

Li Feng1

（ 1. University of South China， Hunan Hengyang 421001）

Abstract：Accord with the tests on asphalt mixture properties with waste glass of different particle size and gradation， characteristic parameters such as relative density， voidage， voids， saturation， Marshall stability as well as flow value were analyzed and compared. It turned out that graded glass had an important effect on asphalt properties， i.e.， voidage， voids， flow value decreased while saturation and stability increased as size increasing. When the size equaled to about 4.75mm， stability values reached maximum ones， but other parameters remained to the code required scope.

Key words： waste glass； particle size and gradation； properties of asphalt mixture

引言

基于可持续发展和绿色发展理念的不断深入，对生产生活中废玻璃的回收与利用引起各国政府与科研学者的高度关注，成为业界的研究重点和焦点。欧美发达国家于上世纪九十年代开展相关研究和实践，并取得一定的阶段性成果[1]。随着我国经济总量和人民生活水平的提高，废玻璃的排放量高达亿吨之上，并呈逐年增加的趋势[2]。实现废玻璃的再利用，对我国的产业结构调整、节能降耗、环境保护等方面具有重要的经济效益和社会效益。

玻璃由二氧化硅、 碳酸钠、铝、硼硅、石英等所组成，主要化学成分为SiO2、CaO、Na2O、Al2O3，具有优粒形、低透水性、耐腐蚀性的特点。废玻璃经破碎筛选后具有与河砂接近的物理性能，且密度与砂相近，可以以一定比例代替骨料[3]，同时其反光性为桥隧路面的照明提供了思路。目前废玻璃沥青混凝土在美国、日本和台湾地区得到广泛应用，认为其路用性能并不亚于普通沥青路面，尤其是夜间的反光使其具有良好的景观效果[4]。……