有色金属大型壁板型材连续轧挤初探

有色金属大型壁板型材连续轧挤初探

钟毅, 陈业高, 潘昇旻, 叶蔚

(昆明理工大学 材料科学与工程学院, 云南 昆明650000)

摘要：利用自行设计改装的连续轧挤设备模拟大型壁板型材的成形.以橡皮泥作为模拟试验材料,在由二辊轧机改装得到的连续轧挤设备上进行试验,模拟了宽×厚为98 mm×1 mm的板材连续轧挤生产过程.橡皮泥模拟试验及连续轧挤的工程法力学分析证明,利用连续轧挤法制备大型壁板型材是可行的,对大型壁板型材的制备有一定的指导作用.

关键词：连续轧挤; 大宽厚比; 物理模拟; 大型壁板型材

收稿日期：2015-04-18

基金项目：云南省教育厅科学研究基金项目(2013Z115)

作者简介：钟毅(1964—),男,教授,主要研究方向为材料成形新工艺与新设备. E-mail:zy5125990@163.com

中图分类号：TG375`+.25

文献标志码：A

Abstract：The processing of large thin-wall wainscot was simulated on the self-made ectrolling device by refitting two roll mills.Selected as simulating materials,plasticine was manufactured into the flat whose width and thickness are 98 mm×1 mm.The experiment and mechanical analysis proved that the extrolling method is feasible for the manufacturing of large wall profiles and physical simulating test plays a guiding role in the production of large thin-wall wainscot of real nonferrous.

Keywords：extrolling; huge width-thickness ratio; physical simulating; large thin-wall wainscot

A Preliminary Study on Extrolling to Manufacture Large Thin-wall Wainscot of Non-ferrousZHONG Yi, CHEN Yegao, PAN Shengmin, YE Wei

(School of Material Science and Engineering, Kunming University of

Science and Technology, Kunming 650093, China)

0引言

铜排是一种大电流以及超大电流导电型材,广泛应用于冶金、电镀和化工等行业,可用于制造高低压电器、配电设备、开关触头和母线槽等.作为大电流导电产品,铜排表面必须光滑,无毛刺、凹坑、棱角,以防在尖端或凹坑部分放电,造成短路.铜排的主要生产方法及相应的产品尺寸见表1.高精度异形铜带用于半导体塑封三极管的引线框架的制作[1],断面有U形、T形、L形、W形和阶梯形.U形铜带规格中宽厚比最大为179,最小为135.异形铜带的生产方法有锤锻法、异形孔型轧制法和铣削法.锤锻法生产的产品表面光滑,尺寸精度高,但要求每分钟锤锻2 000余次,对设备要求较高;异型孔型轧制法生产的产……