大型发电机组冷却系统用3003铝合金型材挤压工艺研究

史玮

摘 要：研究了大型发电机组冷却系统用3003铝合金型材在挤压过程中铸锭温度、挤压速度及拉伸率对型材尺寸、表面质量及性能的影响。结果表明，铸锭加热温度在465℃～475℃时型材表面质量和性能满足技术要求。挤压速度控制在2.0mm/s～2.6mm/s时型材尺寸合格，表面质量良好。调直拉伸率控制在2%型材无扭拧弯曲现象并且尺寸、表面质量及性能均满足技术要求。

关键词：3003铝合金；挤压工艺；型材尺寸；表面质量；性能

中图分类号：TG376 文献标识码：A 文章编号：1671-2064（2017）08-0058-02

Abstract：The effect of cast ingot temperature、extrusion speed and tensile rate of the extrusion process on the profile size、the profile surface quality and the mechanical properties of 3003 aluminum alloy profile for the cooling system of large generators have been studied. The results show that the profile surface quality and the mechanical properties can be guaranteed by the temperature of cast ingot is between 465℃ and 475℃. When the extrusion speed is controlled at 2.0mm/s～2.6mm/s that the sizes of the profile is qualified and the surface quality is good. When the tensile rate is controlled at 2% that the profile without twisting and bending， meanwhile， the profile size、the profile surface quality and the mechanical properties can be can be meet technical requirements.

Key words：3003 aluminum alloy； extrusion process； profile sizes； surface quality； mechanical properties

近幾十年来，国内外发展了许多用于气体、液体的紧凑式传热表面，有效的减少了换热器的几何尺寸，作为高表面面积密度的板翘式换热器就是其中之一。它具有结构紧凑、轻巧传热强度高等特点，适合于大型发电机组冷却系统的应用，是一种具有发展前途的新型电站冷却器设备部件[1]。该散热装置主体基管选用3003材质AL-Mn系合金，是一种应用最广的防锈铝，这类合金的强度不高，不可热处理强化。故选用冷加工方式来提高它的力学性能（H112状态），在半冷作硬化时塑性良好如拉伸调直。常用于要求可塑性高、耐腐蚀性好、焊接性良好的液体或气体介质中工作的低载荷零部件。

1 产品技术要求

1.1 产品特性

型材单重0.72kg/m，定尺11710mm，外形尺寸宽112mm、高12mm、壁厚1mm，支撑筋厚度1.5mm，平面间隙≤0.3mm。该型材因壁厚较薄，材料热挤压状态粘度大，挤压时尺寸公差、形位公差和表面质量要求严格控制难度大，需严格控制生产工艺。

1.2 状态

H112状态适用于热加工成型的产品其力学性能有规定要求。……