铣刨速度对RAP材料影响的试验研究

周小红

摘要：不同的铣刨速度对 RAP材料的性能有着一定的影响，特别是对RAP材料的级配组成有着较大的影响，本研究对不同的旧沥青混凝土路面采用不同的铣刨速度，对铣刨所得的RAP材料进行筛分试验，得到筛孔通过百分率、级配曲线与各粒径范围所占比例，并对以上结果展开研究。从试验结果中，可以得到铣刨速度较低时，不同路面的回收料的级配差异越小，各粒径范围所占比例的波动越小。

Abstract： Different milling speeds have certain influence on the performance of RAP materials， especially the gradation composition of RAP materials. This study used different milling speeds for different old asphalt concrete pavements. The RAP material obtained by milling was subjected to screening test， and the percentage of mesh passage， gradation curve and the proportion of each particle size range were obtained， and the above results were studied. From the test results， it can be found that when the milling speed is low， the gradation difference of the recycled materials of different road surfaces is smaller， and the fluctuation of the proportion of each particle size range is smaller.

关键词：铣刨速度；铣刨料；级配；RAP材料

Key words： milling speed；milling material；grading；RAP material

中图分类号：U414 文献标识码：A 文章编号：1006-4311（2018）28-0171-03

0 引言

自沥青路面再生技术得到应用与推广以来，很多学者对RAP材料性能與回收工艺展开了研究。Kim[1]对将SBS改性沥青作为新沥青与旧RAP拌和后的混合料性能进行了研究，采用APA和IDT对0-35%的旧料掺配率下混合料进行试验，结果表明在所有的旧料掺配率下，混合料都显示出良好的性能。方杨[2]等采用两种铣刨方案对其进行铣刨，对RAP矿料级配、沥青含量、回收沥青性质进行对比研究，对于使用7年左右的沥青混凝土路面，推荐采用全厚度铣刨。张明杰[3]等研究表明与整体铣刨回收相比，采用分层铣刨回收，RAP的油石比、旧沥青各性能指标及旧集料各筛孔通过百分率的变异性均较小。邱胜华[4]等在河南连霍高速公路工程项目沥青路面厂拌冷再生施工中通过精确控制泡沫沥青生产参数、改进旧路面铣刨速度、提高旧路面回收料质量等一系列措施保证了冷再生层质量。

基于国内外的研究，对不同路面与铣刨速度对铣刨料性能的影响研究可提高铣刨料的利用率，控制旧料的变异性。……