酸性地下水对于地下洞室混凝土耐久性的影响

殷苗苗 仇岚 胡坤 王开成 孟繁聪 孙旭伟

【摘 要】近年来定期现场巡查反映：厂房顶拱一定范围内的渗水点在雨季有增多迹象;在厂房周围地下洞室内普遍见有渗水现象，还见有多处析出物，局部区域排水沟已经失去强度呈现粉化状态。长此下去，区内酸性地下水对地下洞室混凝土结构的耐久性产生不利影响，可能会引起洞室塌方，影响洞室的安全稳定运行。

【关键词】地下洞室;混凝土;耐久性;酸性地下水

Abstract：In recent years，regular on-site inspections have reflected there are signs of increase in the rainy season water seepage points within a certain range of roof arches;In the underground caverns around the factory building，there is a common phenomenon of water seepage.There are also many effluents.The local drainage ditch has lost its strength and appears to be powdered.In the long run，the acidic groundwater in the area has a negative impact on the durability of concrete structure in the underground cavern，which may cause cavern collapse and affect the safe and stable operation of the cavern.

Key words：Underground cavern;Concrete;Durability;Acid groundwater

0 引言

江苏宜兴抽水蓄能电站总的运行工况良好，但也出现酸性地下水的腐蚀问题。据区内渗流监测资料，厂房围岩局部渗压值近年来呈现了上升的趋势。地下厂房区围岩的工程特性近年来在酸性水作用下呈现了一定的“弱化”。长此下去，区内酸性地下水对地下洞室区域的混凝土结构耐久性方面产生一定的不利作用，必须引起重视。

截止到目前，回弹法、钻芯法、拔出法、压痕法及超声法等[1]是混凝土损伤方面普遍应用的检测识别普技术方法。但是应用范围有限。XRF、XRD、SEM等测试方法是最近一段时期得到有效应用的方法，主要在矿物相、化学成分等方面对腐蚀性状进行诊断和分析[2，3]。

1 酸性地下水作用下混凝土腐蚀的基本特征

1.1地下洞室混凝土样

根據现场探察，认为在酸性渗漏水作用下地下厂房区不同部位混凝土已经受到了一定程度的腐蚀，并具有如下分布特征：

（1）厂房顶拱部位出现的新老渗水点位及周围区域，其表面混凝土呈现灰白色，是受到酸性腐蚀的较为典型的外观颜色;敲击发现此处混凝土的强度已经弱化。……