玻璃纤维长度和掺量对普通混凝土力学性能的影响

柏青松 汪玲 董叶顺

摘 要：为探究玻璃纤维对普通混凝土的抗压性能及流动性的影响，本试验在6组普通混凝土中分别掺入同掺量不同长度和同长度不同掺量的玻璃纤维。试验结果表明：当掺量相同时，纤维长度在适当范围内可以提高混凝土的抗压强度，但并不是越长越好;长度相同时，适当添加掺量也可以提高混凝土的抗压强度，且玻璃纤维的掺入对混凝土试块的抗压强度影响并不是十分明显。另外，混凝土的流动性会随玻璃纤维掺量的增加而逐渐降低。

关键词：玻璃纤维;普通混凝土;流动性;抗压性能

中图分类号：TU528.572 文献标识码：A 文章编号：1003-5168（2021）22-0078-03

Abstract： In order to explore the influence of glass fiber on the compressive performance and fluidity of ordinary concrete， in this experiment， 6 groups of ordinary concrete were mixed with the same amount of glass fiber with different length and the same length with different dosage. The test results show that when the amount of fiber is the same， the compressive strength can be improved when the fiber length is in the appropriate range， but the longer the better; when the length is the same， the appropriate amount of addition can also increase the compressive strength， and the influence of the incorporation of glass fiber on the compressive strength of the concrete test block is not very obvious. In addition， the fluidity of concrete will gradually decrease with the increase of glass fiber content.

Keywords： glass fiber;ordinary concrete;liquidity;compressive properties

混凝土是现代工程结构的主要材料。近年来，我国每年混凝土用量约15.0×108 m3，用量巨大。以混凝土为主要材料制成的结构广泛应用于建筑、桥梁、隧道、矿井、水利以及港口等工程[1]。但是，单一的普通混凝土材料本身存在抗拉强度普遍较低、延性差、在拉应力或冲击荷载作用下易发生脆性破坏等缺陷，在一定程度上阻碍了混凝土的进一步使用[2]。在普通混凝土中掺入适当的纤维材料形成纤维增强混凝土，其抗拉强度、抗剪强度、抗折强度、抗裂性能和抗疲劳性能等均有较好的提高。目前，工程建设中应用较多的纤维材料，有合成纤维、钢纤维和碳纤维等。随着其他纤维混凝土在建设工程中的成功应用，耐碱玻璃纤维混凝土以其优良的力学性能走进了国内外学术界的研究视野。然而，当前国内外对耐碱玻璃纤维混凝土抗压性能的研究还很少，主要集中在耐碱玻璃纤维布及喷射混凝土等方面[3]。……