基于高酸性条件下元素硫对碳钢腐蚀的影响分析

唐江

【摘  要】天然气中，在硫含量压力条件和温度超标的情况下，都会形成硫沉积现象，在元素硫大量沉积的背景下，会直接造成流体通道堵塞问题，会直接发生采输系统严重腐蚀现象。为解决这种问题，需要通过电化学极化测试方法，全面开展碳钢腐蚀性能实验，对元素硫进行现场的沉积方式模拟，通过这种方法才能发挥出全部的碳钢腐蚀性实验效果，同时也能针对现场产生的沉积方式进行模拟，降低对碳钢腐蚀性能产生的影响。

【Abstract】In natural gas， when the sulfur content pressure condition and temperature exceed the standard， the sulfur deposition phenomenon will be formed. Under the background of a large amount of elemental sulfur deposition， the fluid channel blockage will be directly caused， and the serious corrosion phenomenon of the production and transportation system will directly occur. In order to solve this problem， it is necessary to carry out corrosion test of carbon steel by means of electrochemical polarization test， and simulate the deposition mode of elemental sulfur in situ. Only in this way can we give full play to the corrosion test effect of carbon steel， and at the same time， we can also simulate the deposition mode generated in the field to reduce the influence on the corrosion performance of carbon steel.

【关键词】高酸性条件;元素硫;碳钢腐蚀

【Keywords】high acid condition; elemental sulfur; carbon steel corrosion

【中图分类号】TE980                                             【文献标志码】A                                                 【文章编号】1673-1069（2021）08-0172-02

1 引言

在高含硫天然气中硫含量的温度和压力条件会直接影响最终的硫沉积。具有沉积类型的元素硫，将固态颗粒作为内部不可缺少的重要部分，之后使用硫悬浮溶液，在较高的环境温度下确保硫形式存在的意义，液态硫也会随着温度的改变在管道内壁形成附着，在元素硫大量沉积的背景下，会直接堵塞通道，最终导致关井停产。元素硫不仅会直接堵塞采输系统，同时还会对日常的工作造成影响，对于系统运行也会产生严重腐蚀。在应用元素硫的过程中，需要将重点集中在硫沉积部位，做好局部腐蚀问题处理，对于一些可能发生穿孔的腐蚀部位，需要在管底进行孤立点蚀[1，2]。

2 试验方法

在进入全新发展阶段的背景下，元素硫侵蚀问题已经被人们所重视，并且也逐渐成为世界领域中的研究重点，但是到目前为止仍然没有针对元素硫进行统一的定义，对于腐蚀机理方面认知不够准确。……