液压工程挖掘机车轮钢圈断裂失效分析

朱磊

摘要：液压工程机在工程领域应用非常广泛，其产品质量的可靠性和安全性将为生产建设提供可靠保障。工程机车轮在更换过程中容易发生钢圈断裂的情况，从而会引发安全事故，因此要尽量避免此类事故的发生。文中着重从宏观检查、微观检测、钢圈拉伸试验、钢圈化学成分鉴定等方面分析钢圈断裂失效原因，从而得出断裂的主要原因为钢圈疲劳，锁环表面沟槽圆角处表面存在大量氧化铁杂质，加快了钢圈疲劳速度，加上钢圈生产工艺导致的材质分布不均匀，最终造成钢圈发生疲劳断裂状况。

Abstract： Hydraulic engineering machines are widely used in the engineering field， and the reliability and safety of their product quality will provide a reliable guarantee for production and construction. Construction locomotive wheels are prone to breakage of steel rims during the replacement process， which will cause safety accidents. Therefore， it is necessary to avoid such accidents as much as possible. This article focuses on analyzing the reasons for the failure of the steel ring from the aspects of macroscopic inspection， microscopic inspection， steel ring tensile test， and chemical composition identification of the steel ring. It is concluded that the main cause of the fracture is steel ring fatigue， and the surface of the groove on the surface of the lock ring There are a large amount of iron oxide impurities， which speeds up the fatigue rate of the steel ring， and the uneven material distribution caused by the steel ring production process will eventually cause the steel ring to undergo fatigue fracture.

關键词：工程机车轮;钢圈;断裂;失效性分析

Key words： engineering locomotive wheel;steel ring;fracture;failure analysis

中图分类号：TU621                                     文献标识码：A                                文章编号：1674-957X（2021）14-0123-02

0  引言

国民经济的发展离不开各种各样的工程机车，尤其是液压工程机车在工程领域应用十分广泛。而机车设备的安全可靠运转是保证安全生产的必要条件。然而由于生产工艺的差异和工作环境的优劣，工程设备的零部件都会不同程度的出现磨损和失效，从而会引发各种意外事故，甚至威胁着运行操作人员的生命安全。因此必须重视设备零部件的失效问题，找出根源，不断改进和完善，提高产品质量。产品失效性分析是质量监督管理的重要环节，在质量鉴定工作中被广泛采纳和应用。本文将通过实例来分析钢圈断裂的原因，从来说明钢圈失效性分析的重要性和必要性。

1  失效性分析概述

失效性分析是广泛应用于各领域的一种重要的方式，是一门发展中的新兴学科。……