涤纶长纤织物的收缩性能

黄战伟

摘要：针对化纤长纤织物在不同的温度，和碱的作用下，织物经纬向的收缩比例，方便工艺设计者合理设计染缸的生产工艺。结果显示涤纶织物在NAOH一定比例的作用下，随着温度的升高，经纬逐渐开始收缩，不同的温度点，纤维收缩比列不一致，收缩比例快的温度点，我们定为恒温段点，达到一定温度后，收缩闭合，此温度点便是最高温度点。

关键词：涤纶长纤;梭织;前处理;收缩;温度

Abstract： It is convenient for the process designer to design the production process of dyeing cylinder for the shrinkage ratio of chemical fiber long-fiber fabric under different temperature and alkali action.The results showed that under the action of a certain proportion of NAOH， the warp and weft gradually began to contract with the increase of temperature. At different temperature points， the fiber shrinkage ratio was not consistent， and the temperature with a fast shrinkage ratio was set as the constant temperature segment point. After reaching a certain temperature， the shrinkage closed， which was the highest temperature point.

前言

滌纶长纤织物在实际染整加工过程中，容易发生直条皱，皱印等染色疵病，或者出现由于温度设计不合理，纤维收缩不到位造成的手感不符，经纬密度不对。对后续的染整加工造成很大影响。原因在于工艺设计者对纤维的性能不了解，未做实验，便下达工艺。收缩点未控制，保温点未找到，收缩快的温度点升温比例太快导致。

本实验在浴比恒定下，NAOH条件下，不同比例的涤纶织物在各种温度下的收缩表现

1 试验部分

1.1 材料

1.2 仪器及设备

小样机 电子称 量尺

1.3 试验方法

1.3.1 白坯布平整机平整-取样布（每种布样取10块）→每块布上经纬向表明10cm→在每块布上标明顺序→进入小样机→放入助剂→升温到相应温度→降温→洗布→取出布样烘干→测量每块布经纬向长度

1.3.2 工艺处方

1.4 测试方法

1.4.1 测试每块布收缩前和收缩后的比例 收缩前W 收缩后W0 测收缩率为

收缩率 = W-W0/W ×100%

1.4.2检测丙烯酸浆料残留

取每块样5G 加入0.02 % owf 阳离子染料 加热至100度检测，根据每块布颜色的深浅判断浆料残留情况

2试验过程

2.1规……