热水锅炉腐蚀问题成因及对策探析

【摘要】热水锅炉的腐蚀问题一直备受关注，即使是生产厂家和型号都相同的锅炉，由于使用环境的差异，腐蚀程度也会各不相同。所造成的影响和后果也各不相同，只有深入了解腐蚀的根本成因，做到防患于未然，才能保障锅炉的安全运行以及生产的顺利进行。本文就热水锅炉腐蚀问题成因及对策展开探讨，并提出相应的防治和预防措施。

【关键词】热水锅炉；腐蚀；分析

【DOI编码】10.3969/j.issn.1674-4977.2023.04.034

Analysis on the Causes and Countermeasures of Corrosion in Hot Water Boilers

LI Bin

（Haicheng Boiler and Pressure Vessel Inspection Institute， Haicheng 114201， China）

Abstract： The corrosion problem of hot water boilers has always been a concern， and even boilers with the same manufacturer and model may have varying degrees of corrosion due to differences in operating environments. The impact and consequences are also different. Only by deeply understanding the fundamental causes of corrosion and taking preventive measures can we ensure the safe operation of boilers and the smooth progress of production. This article explores the causes and countermeasures of corrosion in hot water boilers， and proposes corresponding prevention and control measures.

Key words： hot-water boiler； corrosion； analysis

1熱水锅炉的腐蚀问题及成因

北方冬季供暖很大一部分都在应用着热水锅炉，热水锅炉的安全运行就决定了供暖的顺利进行和百姓的安居乐业。腐蚀是热水锅炉的一个重大安全隐患，如何排除、解决就尤为重要。热水锅炉的腐蚀问题主要分为内部腐蚀和外部腐蚀两大类。

1.1内部腐蚀

主要有垢下腐蚀、氧腐蚀、二氧化碳腐蚀、冲刷腐蚀、酸腐蚀、碱腐蚀等。

1.1.1垢下腐蚀

热水锅炉的介质是水，它的来源主要是地下水，而地下水中含有大量的杂质，这些杂质中的悬浮物质及某些胶体物质可直接沉着吸附于受热面形成污垢，也有很多的溶解物质随着温度升高溶解度降低析出，沉积在锅炉内壁。北方的水质硬度较大，可以分为碳酸盐硬度和非硫酸盐硬度，水中的钙镁离子成分含量较大，成分的物质以钙镁的重硫酸盐或强酸盐为主。难以溶解的化合物析出时以水渣形式出现，如果不能及时排除就会转变为二次硬质水垢，这些形成的水垢会造成垢下腐蚀，相应地发生化学或电化学腐蚀，水垢的发生会造成锅炉内壁受热面不能被水及时冷却，而使锅炉受热面长时间超温，最终导致蠕胀变形甚至产生裂纹破裂。……