中图分类号： TG146.1+1 文献标志码：A 文章编号：1004-4345（2025）02-0011-05

Production Process for Ultra-Thin High-Performance Tin-Phosphor Bronze Strips

TIAN Juntao

（China Nerin Engineering Co.，Ltd.，Nanchang，Jiangxi 33Oo38，China）

Abstract Thepaper makesastudyof the keyproduction processof ultra-thin high-performance tin-phosphor bronze strip （C5210alloy）andproposesastrippreparatioprocess withathicknessofO045＼～0.10mmthroughsystematicexperimentsanddata analysis. The results show that the strip products with tensile strength of ⩾830 MPa and surface hardness of ⩾ HV230 can be obtained by optimizing various procedures and operations，including burdening ratio （outsourced old materials of ⩽50% ）， smelting and casting （casting temperature of 1 180 C ， casting speed of 155 mm/min）， homogenizing annealing （670 Cx8.5 h） and rough rolling （size of 3.000 mm）， intermediate rolling （size of 1.000mm ）and finish rolling （size of 0.045 mm）， etc.

Keywords ultra-thin; copper strip; tin-phosphor bronze strip; rolling; process

加工工艺及试验方案

锡磷青铜合金带材具有高强度、高弹性，优异的耐磨性和抗磁性，同时兼具良好的冷加工性、耐蚀性、焊接性和切削加工性，广泛应用于弹性元件、精密仪器仪表中的耐磨件和抗磁零件的制造。目前，市场主流产品C5191带材的厚度规格为 0.15～ 0.30mm 。该型号带材生产技术成熟，平均加工费约6000元/t。受产能过剩影响，行业竞争加剧，加工费逐年降低。为提高盈利空间，铜加企业正逐步将焦点转向利用先进设备生产高附加值的超薄锡磷青铜带材。经市场调研，厚度在 0.045～0.100mm 的超薄C5210带材，市场加工费约15000元/t。因此，开发0.045～0.100mm 超薄C5210锡磷青铜带材生产工艺，对丰富产品规格、提升企业效益具有重要意义。

1.1铸坏试验方案

本试验采用T2角料/镀锡线 + 光亮线 + 青铜铣屑 + 青铜外料 + 青铜回料的原料搭配组合进行铸坯。熔炼工艺主要参数如下：1）加料顺序。阴极铜或旧料 煅烧木炭覆盖 熔化 添加 1/2P-Cu⟶ 添加锡 添加 1/2P-Cu⟶ 搅拌 升温 检验分析 成分调整 升温扒渣 煅烧木炭覆盖 静置 转炉。2）合金配料方案。本试验C5210合金采用了两种配料方案，具体见表1。3）熔化炉、转炉温度。熔化炉、转炉温度控制在 1230～1250^∘C4 熔体覆盖。熔化炉采用木炭覆盖，厚度为 80～100mm ；保温炉采用木炭覆盖，厚度为 60～80mm 5）保温炉液面高度控制。保温炉内铜液面距炉顶不小于 450mm 。具体参数见表2。

1.2均匀化退火工艺

锡磷青铜合金结晶温度范围较宽，其中低熔点的Sn和P元素扩散速度较慢，在合金凝固时易出现严重的反偏析现象。……